Celcon® GB10
乙缩醛（POM）共聚物
Ticona
产品说明
Celcon® GB10 is a 10% glass bead filled grade for low shrinkage and warp resistance in large, flat, and thin walled parts.
Chemical abbreviation according to ISO 1043-1: POM
总体
材料状态 • 已商用：当前有效
供货地区 • 北美洲 • 拉丁美洲 • 南美洲
填料/增强材料 • 玻璃珠, 10% 填料按重量
性能特点 • 抗弯曲 • 收缩性低
用途 • 薄壁部件
RoHS 合规性 • 联系制造商
形式 • 颗粒料
加工方法 • 注射成型
树脂ID (ISO 1043) • POM
物理性能 额定值单位制 测试方法
密度 1.47g/cm³ ISO 1183
溶化体积流率（MVR） (190°C/2.16 kg) 17.0cm³/10min ISO 1133
收缩率 ISO 294-4
横向流量 1.6%
流量 1.9%
机械性能 额定值单位制 测试方法
拉伸模量 3100MPa ISO 527-2/1A/1
拉伸应力 (屈服) 55.0MPa ISO 527-2/1A/50
拉伸应变 ISO 527-2/1A/50
屈服 7.0%
断裂 10%
冲击性能 额定值单位制 测试方法
简支梁缺口冲击强度 (23°C) 3.5kJ/m² ISO 179/1eA
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 94.0°C ISO 75-2/A
熔融温度 2 166°C ISO 11357-3
注射 额定值单位制
加工（熔体）温度 182 到 199°C
模具温度 82.0 到 93.0°C
注射说明
Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the material.
Melt Temperature: Preferred range 182-199 C (360-390 F). Melt temperature should never exceed 230 C (450 F).
Mold Surface Temperature: Preferred range 82-93 C (180-200 F) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120 C (250 F) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65 C/150 F) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25 C (80 F). In general, mold surface temperatures lower than 82 C (180 F) may hinder weld line formation and produce a hazy surface or a surface with flow lines, pits and other included defects that can hinder part performance.
备注
1 一般属性：这些不能被视为规格。
2 10°C/min
1 / 1
|