Hostaform® C 9021 10/1570
乙缩醛（POM）共聚物
Ticona
产品说明
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GCL, 03-002
POM copolymer
Standard Injection molding type, UV-stabilized with carbon black good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance high resistance to thermal and oxidative degradation.
UL-registration for a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B electrical 110 °C, mechanical 90 °C.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.
Ranges of applications: exterior applications.
UL = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
总体
材料状态 • 已商用：当前有效
供货地区 • 非洲和中东 • 欧洲 • 亚太地区
添加剂 • 碳黑 • 紫外线稳定剂
性能特点 • 共聚物 • 耐热性，高 • 耐油
• 抗溶解性 • 耐水解性
用途 • 室外应用
RoHS 合规性 • 联系制造商
加工方法 • 注射成型
树脂ID (ISO 1043) • POM
物理性能 额定值单位制 测试方法
密度 1.42g/cm³ ISO 1183
溶化体积流率（MVR） (190°C/2.16 kg) 8.00cm³/10min ISO 1133
收缩率 ISO 294-4
横向流量 1.8%
流量 2.0%
吸水率 (饱和, 23°C) 0.65% ISO 62
机械性能 额定值单位制 测试方法
拉伸模量 3000MPa ISO 527-2/1A/1
拉伸应力 (屈服) 64.0MPa ISO 527-2/1A/50
拉伸应变 (屈服) 8.0% ISO 527-2/1A/50
断张率 25% ISO 527-2/1A/50
拉伸蠕变模量 ISO 899-1
1 hr 2500MPa
1000 hr 1400MPa
冲击性能 额定值单位制 测试方法
简支梁缺口冲击强度 ISO 179/1eA
-30°C 6.0kJ/m²
23°C 6.5kJ/m²
简支梁缺口冲击强度 ISO 179/1eU
-30°C 110kJ/m²
23°C 110kJ/m²
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 105°C ISO 75-2/A
维卡软化温度 150°C ISO 306/B50
熔融温度 2 167°C ISO 11357-3
线形膨胀系数 - 流动 0.00011cm/cm/°C ISO 11359-2
1 / 2
Hostaform® C 9021 10/1570 2012年10月6日
乙缩醛（POM）共聚物
Ticona
电气性能 额定值单位制 测试方法
表面电阻率 1.0E+14ohm IEC 60093
体积电阻率 1.0E+14ohm•cm IEC 60093
耐电强度 28kV/mm IEC 60243-1
漏电起痕指数 300V IEC 60112
可燃性 额定值单位制 测试方法
UL 阻燃等级 UL 94
1.50 mm HB
3.00 mm HB
补充信息 额定值单位制 测试方法
ISO Type POM-K, M-GCL, 03-002 ISO 9988-1
注射 额定值单位制
加工（熔体）温度 190 到 230°C
模具温度 80.0 到 120°C
螺杆长径比 15.0:1.0 to 25.0:1.0
注射说明
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
备注
1 一般属性：这些不能被视为规格。
2 10°C/min
|