Hostaform® C 9021 S1
乙缩醛（POM）共聚物

Ticona

产品说明

POM copolymer

Standard-Injection molding type with high rigidity, hardness and toughness; good chemical resistance. Modified with 1% silicon oil Available in natural and colored

Fulfils EG-directive 10/2011 as well as the recommendation XXXIII for consumer goods of the BfR, FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 < 100mm/min for a thickness more than 1 mm.

Ranges of applications: precision engineering, electric and electronical industry, domestic appliances.

FDA = Food and Drug Administration (USA)
BfR = Bundesinstitut für Risikobewertung (Germany) FMVSS = Federal Motor Vehicle Safety Standard (USA)

总体

材料状态 • 已商用：当前有效    
供货地区 • 北美洲 • 欧洲   
添加剂 • 硅酮润滑剂    
性能特点 • High Hardness • 经润滑  • 韧性良好 
 • 刚性，高 • 耐化学性良好   
     
用途 • 电气/电子应用领域 • 工程配件  • 家电部件 
机构评级 • BgVV Recommendation XXXIII • EU 10/2011  • FDA 21 CFR 177.2470 
RoHS 合规性 • 联系制造商    
外观 • 可用颜色 • 自然色   
加工方法 • 注射成型    
     
物理性能  额定值单位制  测试方法 
密度  1.41g/cm³  ISO 1183 
收缩率    ISO 294-4 
横向流量  1.8%   
流量  2.0%   
吸水率 (饱和, 23°C)  0.65%  ISO 62 
机械性能  额定值单位制  测试方法 
拉伸模量  2700MPa  ISO 527-2/1A/1 
拉伸应力 (屈服)  60.0MPa  ISO 527-2/1A/50 
拉伸应变 (屈服)  12%  ISO 527-2/1A/50 
断张率  35%  ISO 527-2/1A/50 
冲击性能  额定值单位制  测试方法 
简支梁缺口冲击强度    ISO 179/1eA 
-30°C  6.0kJ/m²   
23°C  6.5kJ/m²   
简支梁缺口冲击强度    ISO 179/1eU 
-30°C  160kJ/m²   
23°C, 局部断裂  180kJ/m²   
热性能  额定值单位制  测试方法 
熔融温度 2  166°C  ISO 11357-3 
线形膨胀系数    ISO 11359-2 
流动  0.00011cm/cm/°C  
横向  0.00011cm/cm/°C  
可燃性  额定值单位制  测试方法 
燃烧速率 (1.00 mm)  < 100mm/min ISO 3795 
充模分析  额定值单位制  测试方法 
熔体密度  1.20g/cm³  Internal Method 
熔体导热性  0.16W/m/K  Internal Method 
顶出温度  165°C   
1 / 2     
   
    
    
   
    
 
Hostaform® C 9021 S1  2012年10月6日
乙缩醛（POM）共聚物  
Ticona  
充模分析 额定值单位制 测试方法
Specific Heat Capacity of Melt 2210J/kg/°C Internal Method
补充信息 额定值单位制 测试方法
Effective Thermal Diffusivity 4.85E-8m²/s Internal Method

备注
1 一般属性：这些不能被视为规格。

2 10°C/min