拉丝级聚酰胺 66/6 共聚物，单丝，真空袋薄膜，多层薄膜

 

Vydyne® 840F

聚酰胺 66/6 共聚物

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

Vydyne 840F is a PA66-based copolymer that features high melt strength, shear thinning behavior, high tensile strength, ductility, and slow crystallinity that matches crystallization temperatures/rates very close to that of ethylenes. The combination of properties exhibited by Vydyne 840F make it a good candidate for a number of applications such as numerous film uses, sheeting, and monofilament. The slow crystallization behavior coupled with the melting point ~ 215-220°C and great mechanical properties makes this material extremely useful for outside layers or internal layers of the multilayer film. This material further exhibits a very high elongation to break (> 500%) allowing for high draw ratios for thermoforming or when orienting the film.

总体

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

添加剂 • 热稳定剂

特性 • High Toughness • 高熔体强度 • 抗穿孔性

• 高强度 • 较高的熔体稳定性 • 耐化学性良好

• 棒材 • 工业应用 • 型材

用途 • 单丝 • 管件

• 真空袋薄膜

• 多层薄膜 • 片材

机构评级 • ASTM D4066 PA0111 • EC 1935/2004 • MIL M-20693B

• ASTM D6779 PA0111 • EU 2023/2006 • 欧洲 10/1/2011 12:00:00 AM

RoHS 合规性 • RoHS 合规

外观 • 自然色

形式 • 粒子

加工方法 • 吹塑薄膜 • 流延薄膜

• 挤出 • 型材挤出成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.14 -- g/cm³ ISO 1183

含水量 0.10 -- % ASTM D6869

体积密度 674 -- g/l ASTM D1895

相对粘度

(Formic Acid) 115 到 145 -- ASTM D789

(Sulphuric Acid) 3.80 到 4.10 -- ISO 307

薄膜 干燥 调节后的 单位制 测试方法

膜刺穿力 ASTM F1306

1.0 mil (25 µm), Biaxially Oriented Film -- > 517 lbf

(> 2300) (N)

割线模量 ASTM D882

MD : 1.0 mil (25 µm), Biaxially Oriented Film -- 421000 psi

(2900) (MPa)

MD : 1.5 mil (38 µm), 铸造薄膜 -- 58000 psi

(400) (MPa)

TD : 1.0 mil (25 µm), Biaxially Oriented Film -- 435000 psi

(3000) (MPa)

TD : 1.5 mil (38 µm), 铸造薄膜 -- 58000 psi

(400) (MPa)

 

 

 

Vydyne® 840F

聚酰胺 66/6 共聚物

Ascend Performance Materials Operations LLC

薄膜 干燥 调节后的 单位制 测试方法

抗张强度 ASTM D882

MD : 断裂, 0.98 mil (25 µm), Biaxially Oriented -- 34800 psi

Film (240) (MPa)

MD : 断裂, 1.5 mil (38 µm), 挤塑薄膜 -- 14500 psi

(100) (MPa)

TD : 断裂, 0.98 mil (25 µm), Biaxially Oriented -- 39200 psi

Film (270) (MPa)

TD : 断裂, 1.5 mil (38 µm), 挤塑薄膜 -- 14500 psi

(100) (MPa)

伸长率 ASTM D882

MD : 断裂, 0.98 mil (25 µm), Biaxially Oriented -- 140 %

Film

MD : 断裂, 1.5 mil (38 µm), 挤塑薄膜 -- > 500 %

TD : 断裂, 0.98 mil (25 µm), Biaxially Oriented -- 130 %

Film

TD : 断裂, 1.5 mil (38 µm), 挤塑薄膜 -- > 500 %

落锤冲击 (1.5 mil (38 µm), 铸造薄膜) -- > 2000 g ASTM D1709A

埃尔曼多夫抗撕强度 ASTM D1922

MD : 1.5 mil (38 µm), 铸造薄膜 -- 140 g

TD : 1.5 mil (38 µm), 铸造薄膜 -- 150 g

自由收缩 ASTM D1204

MD, 320°F (160°C), Biaxially Oriented Film -- 2.0 %

TD, 320°F (160°C), Biaxially Oriented Film -- 1.0 %

热性能 干燥 调节后的 单位制 测试方法

熔融温度 428 -- °F ISO 11357-3

(220) (°C)

挤出 干燥(英制) 干燥(公制)

干燥温度 158 到 176°F 70 到 80°C

干燥时间 0.0 到 4.0hr 0.0 到 4.0hr

挤压说明

Recommended Extrusion Conditions:

 

Melt Point: 220°C

Cylinder Temperature: 230°C to 275°C

Die Temperature: 240°C

Melt Pressure: 3 to 17 MPa

Blow Film Bath Temperature: 5°C to 20°C

Chill Roll Temperature (Cast Film): 20°C to 40°C (clear), 80°C to 100°C (high stable)

 

Recommended Process Moisture: 0.03 to 0.08%

Screw Design: General Purpose or Barrier

 

 

 

 

 

 

 

拉丝级PA66/6,拉单丝PA66/6,拉细丝PA66/6，拉鬃丝PA66/6,拉地毯丝PA66/6,拉棕丝PA66/6，无纺布PA66/6，纺织业PA66/6,纤维PA66/6,PA66/6刷毛丝,拉丝级聚酰胺 66/6 共聚物，拉丝级聚酰胺 66/6 共聚物 Vydyne® 840F是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581